특성 |
시험수치 |
시험조건 |
시험방법
|
| |
1MIL TYPE
A |
|
|
인장강력
(MD) |
25,000
PSI |
25℃ |
ASTM
D882-64P METHOD A - 100%/MIN |
3%
신장강력
(MD) |
13,000 PSI |
25℃ |
ASTM
D882-64P METHOD A - 100%/MIN |
5%
신장강력
(MD) |
15,000
PSI |
25℃ |
ASTM
D882-64P METHOD A - 100%/MIN |
신장율
(MD) |
160% |
25℃ |
ASTM
D882-64P METHOD A - 100%/MIN |
인장계수
(MD) |
500,000
PSI |
25℃ |
ASTM
D882-64P METHOD A - 100%/MIN |
| 충격강도 |
6.0 KG CM/MIL |
25℃ |
DU
PONT PNEUMATIC IMPACT |
접합내구력
(MIT) |
100,000
CYCLES |
25℃ |
ASTM
D2176-63T (1KG LOADING) |
찢김
저항강도
(GRAVE) |
20 GM/MIL |
25℃ |
ASTM D1922-61T |
| 초기
찢김 저항강도(GRAVES) |
800
GM.MIL |
25℃ |
ASTM
D1004-61 |
연속적
찢김 저항가강도
(ELEMENDORE) |
1,800 LBS/IN |
25℃ |
|
| 초기
파열강도 (MULLEN) |
66
PSI |
25℃ |
ASTM
D774-63T |
| 밀도 |
1,395 |
25℃ |
ASTM
D1505-63T |
마찰계수
(KINETIC)
(FILM TO FILM) |
4.5 |
25℃ |
ASTM
D1894-63 |
| 반사계수
(ABBE) |
1.64 ND25 |
25℃ |
ASTM
D542-50 |
AREA
FACTOR
(SO. IN. /LBS/MIL) |
20,000 |
25℃ |
CALULATION |